Ceramic coated rollers have outstanding advantages, including:
- Specially structured and arranged ceramic plates are incorporated on a characteristic rubber base that increases the coefficient of friction between them and the conveyor. Minimize sliding friction between roller and conveyor, minimize conveyor slip during operation.
- The high wear resistance of the ceramic surface is applied to the drive roller of the conveyor system, making the service life of the drive roller much longer than that of the traditional rubber coated roller.
- Especially in conveyor routes with high conveyor speed and long belt length, under the same load, ceramic coated rollers will reduce conveyor tension and prolong conveyor life compared to high coated rollers. su.
- Reduces conveyor belt deflection and wear during operation.
- Each ceramic rubber sheet has grooves at a certain distance, which can cause foreign substances (dust, soil, materials…) to stick on the roller according to the groove, so the roller has a unique self-cleaning function, Especially suitable for wet working environment.
- Improve operational efficiency, make the roller and conveyor run synchronously to ensure the conveyor operates efficiently and withstands large loads.
| No. | Specifications | Unit | Testing standards | Target level |
| 1 | Rubber hardness | Shore A | TCVN 1595-2:2013 | 60-80 |
| 2 | Rubber elongation at break | % | TCVN 4509:2013 | ≥ 350 |
| 3 | Rubber breaking strength | MPa | TCVN 4509:2013 | ≥ 15,0 |
| 4 | Abrasion | mm³ | TCVN 5363-2013 | ≤ 150 |
| 5 | Adhesion with steel surface | Kg/cm² | TCVN 10230:2013 | ≥ 3 |
Specifications of rubber material coated with rollers
1.1. ABRASION RESISTANCE
1.2. FIRE RESISTANT CORE
1.3. HEAT RESISTANCE
| 1 | Rubber hardness | Shore A | TCVN 1595-2:2013 | 60-80 |
| 2 | Rubber elongation at break | % | TCVN 4509:2013 | ≥ 350 |
| 3 | Rubber breaking strength | MPa | TCVN 4509:2013 | ≥ 15,0 |
| 4 | Abrasion | mm³ | TCVN 5363-2013 | ≤ 150 |
| 5 | Adhesion with steel surface | Kg/cm² | TCVN 10230:2013 | ≥ 3 |
| 6 | Criteria for fire resistance of coated rubber | – | ISO 340:2007 | Đạt |
| 7 | Surface resistance | MΩ | ISO 284:2003 | ≤ 300 |
| 1 | Hardness | Shore A | TCVN 1595-2:2013 | 65±5 |
| 2 | Rubber breaking strength | MPa | TCVN 4509:2013 | ≥ 14 |
| 3 | Rubber elongation at break | % | TCVN 4509:2013 | ≥ 350 |
| 4 | Abrasion | mm³ | TCVN 5363-2013 | ≤ 150 |
| 5 | Adhesion with steel surface | Kg/cm² | TCVN 10230:2013 | ≤ 3 |
| 6 | Working temperature | °C | – | ≤ 150 |